- Induction Shrink Fit Steel Flange Class: Induction Shrink Fitting
Intro: Shrink Fit Steel Flange Objective To heat steel flange for heat shrink application. Reaching the desired temperature results in adequate expansion to allow for placing of the flange over a graphite seal.Material Graphite seal 1” (25.4mm) diameter ste…
- Induction Shrink Fit Steel Tube Class: Induction Shrink Fitting
Intro: Shrink Fit Steel Tube Objective Heating a steel tube to 500-1000F for a shrink-fitting application. Determine expansion (growth) of ID at varying temperatures.Material Steel tubes 7” OD x 4.75” ID x 5” heat zone Type ‘K’ thermocouple to measure t…
- INDUCTION HARDENING OF BEARING PARTS Class: Induction Hardening
Intro: INDUCTION HARDENING OF BEARING PARTS It is known that induction heating is effective in flow-line mass production that precludesresetting of equipment, or in individual production where the application of ordinaryheating methods is difficult.Induction…
- HEAT TREATMENT WITH INDUCTION HEATING OF WITHIN PIPES Class: Induction Thermal Treatment
Intro: HEAT TREATMENT WITH INDUCTION HEATING OF WITHIN PIPES Electrically welded pipes with an external diameter of 16-102 mm made from corrosionresistantsteels of the austenitic class after having been made on argon-arc welding mill(AAW) are at present heat…
- Induction Melting Ticonium and Nobilium Class: Induction Melting
Intro: Melting Ticonium and Nobilium Objective: Crucible melting of Ticonium and Nobilium ingots within a period of 45 seconds. Four ingots of Nobilium are to be placed in a crucible (ID#6012) and heated, while a single ingot of Ticonium is placed in a cruci…
- Induction Melting aluminum for casting Class: High Capacity Melting
Intro: Melting aluminum for casting Objective Heating a graphite crucible to 1292F (700C) to melt aluminum to liquid form for a casting applicationMaterial 9.8” (250mm) OD, 22.4” (570mm) long, 0.7” (17.5mm) thick Graphite crucible, approx. 92.5lb (42kg) o…
- Induction Melting lead ingots Class: Induction Melting
Intro: Melting lead ingots Objective Melting 30 lb(13.6 kg) & 60 lb(27.2 kg) lead ingots to formbattery posts & connectorsMaterial 30 lb(13.6 kg) & 60 lb(27.2 kg) lead ingots and 5” (12.7cm) IDZircar Ceramic Alumina tubeTemperature 620 FFrequenc…
- Induction Crucible melting Class: Induction Melting
Intro: Crucible melting Objective Heat to melting point various materials in a nitrogen atmosphere in a graphite or molybdenum crucible.Material Magnesium fluoride, tantalum pentoxide, aluminum, yttrium fluoride, germanium, hafnium or titanium dioxide and a …
- Induction Bonding plastic handle to knife Class: Induction Bonding
Intro: Bonding plastic handle to knife Objective Bonding handle of a stainless steel surgical knife into a plastic handleMaterial Plastic tool handle, 0.125” (3.18mm) diameter steel knifeTemperature 450 F (232 C)Frequency 390 kHzEquipment • Power of 6 kW i…
- Induction Heating Graphite Susceptor Class: Other Induction Applications
Intro: Heating Graphite Susceptor Heating Graphite SusceptorObjectiveTo Heat a graphite susceptor to 1100C in an inert atmosphere of Nitrogen and Hydrogen. The susceptor is to be used for metal oxide chemical vapor deposition (MOCVD) crystal growth experimen…
Recommended
Air Cooled clamp coil (half-open coil) for preheating gas pipeline
U shape air cooled induction coil by UM-100C-HF for pipeline preheating
induction brazing diamond segment
induction melting for crystal growth
induction unassemble 2Ton guard ring of turbine
induction preheating D5000mm end ring for welding by 2 UM-DSP80A-HF at the same time
induction preheating D1219mm pipeline for welding by UM-DSB80AB-MF air cooled induction heater and i
induction preheating and heat treatment for 18Ton control valve of 600MW turbine