Keywords"in",total
3004 records
-
induction shrink fit steel flange
Shrink Fit Steel Flange Objective To heat steel flange for heat shrink application. Reaching the desired temperature results in adequate expansion to allow for placing of the flange over a graphite seal.Material Graphite seal 1” (25.4mm) diameter steel fl…
-
induction shrink fit steel tube
Shrink Fit Steel Tube Objective Heating a steel tube to 500-1000F for a shrink-fitting application. Determine expansion (growth) of ID at varying temperatures.Material Steel tubes 7” OD x 4.75” ID x 5” heat zone Type ‘K’ thermocouple to measure temper…
-
induction hardening of bearing parts
INDUCTION HARDENING OF BEARING PARTS It is known that induction heating is effective in flow-line mass production that precludesresetting of equipment, or in individual production where the application of ordinaryheating methods is difficult.Induction hard…
-
heat treatment with induction heating of within pipes
HEAT TREATMENT WITH INDUCTION HEATING OF WITHIN PIPES Electrically welded pipes with an external diameter of 16-102 mm made from corrosionresistantsteels of the austenitic class after having been made on argon-arc welding mill(AAW) are at present heat-trea…
-
induction melting ticonium and nobilium
Melting Ticonium and Nobilium Objective: Crucible melting of Ticonium and Nobilium ingots within a period of 45 seconds. Four ingots of Nobilium are to be placed in a crucible (ID#6012) and heated, while a single ingot of Ticonium is placed in a crucible (…
-
induction melting aluminum for casting
Objective Heating a graphite crucible to 1292F (700C) to melt aluminum to liquid form for a casting applicationMaterial 9.8” (250mm) OD, 22.4” (570mm) long, 0.7” (17.5mm) thick Graphite crucible, approx. 92.5lb (42kg) of aluminumTemperature 1292 F (700C…
-
induction melting lead ingots
Melting lead ingots Objective Melting 30 lb(13.6 kg) & 60 lb(27.2 kg) lead ingots to formbattery posts & connectorsMaterial 30 lb(13.6 kg) & 60 lb(27.2 kg) lead ingots and 5” (12.7cm) IDZircar Ceramic Alumina tubeTemperature 620 FFrequency 10 …
-
induction crucible melting
Crucible melting Objective Heat to melting point various materials in a nitrogen atmosphere in a graphite or molybdenum crucible.Material Magnesium fluoride, tantalum pentoxide, aluminum, yttrium fluoride, germanium, hafnium or titanium dioxide and a Pyrex…
-
induction bonding plastic handle to knife
Bonding plastic handle to knife Objective Bonding handle of a stainless steel surgical knife into a plastic handle Material Plastic tool handle, 0.125” (3.18mm) diameter steel knife Temperature 450 F (232 C) Frequency 390 kHz Equipment • Power of…
-
induction heating graphite susceptor
Heating Graphite Susceptor Heating Graphite SusceptorObjectiveTo Heat a graphite susceptor to 1100C in an inert atmosphere of Nitrogen and Hydrogen. The susceptor is to be used for metal oxide chemical vapor deposition (MOCVD) crystal growth experiments. V…